Subsequently, a conventional photoresist spin coater was used to deposit the aged ZnO solution on the cleaned substrates

at 3,000 rpm for 20 s. A drying process was then performed on a hot plate at 150°C for 10 min. The same coating process was repeated thrice to obtain thicker and more homogenous ZnO films. The coated films were annealed at 500°C for Selumetinib mouse 2 h to remove the organic component and solvent from the films. The annealing process was conducted in the conventional furnace. The preparation of the ZnO thin films is shown in Figure 1. Figure 1 ZnO thin film preparation process flow. ZnO NRs formation After the uniform coating of the ZnO nanoparticles on the substrate, the ZnO NRs were obtained through hydrothermal growth. The growth solution consisted of an aqueous solution of zinc nitrate hexahydrate, which acted as the Zn2+ source, and hexamethylenetetramine (HMT). The concentration of the Zn (NO3)2 was maintained at 35 mM, and the molar ratio of the Zn (NO3)2 to HMT was 1:1. For the complete dissolution of the Zn (NO3)2 and HMT powder in DIW, the resultant solution was stirred using a magnetic

stirrer for 20 min at RT. The ZnO NRs were grown by immersing the substrate with the seeded layer that was placed upside down in the prepared aqueous solution. During the growth process, the aqueous solution was heated at 93°C for 6 h in a regular laboratory oven. After the growth process, the samples were thoroughly rinsed with DIW to eliminate the residual salts see more from the surface of the samples and then dried with a blower. Finally, the ZnO NRs on the Si substrate were heat-treated at 500°C for 2 h. The growth process CP673451 research buy of the ZnO NRs is presented in Figure 2. Figure 2 ZnO NR growth process. Material characterization The surface morphology of the ZnO NRs was analyzed using scanning electron microscopy (SEM, Hitachi SU-70, Hitachi, Ltd, Minato-ku, Japan). X-ray diffraction (XRD, Bruker D8, Bruker AXS, Inc., Madison, WI, USA) with a Cu Kα radiation (λ = 1.54 Ǻ) was used to study the crystallization and structural properties of the NRs. The absorbed chemical SGC-CBP30 compounds that exited on the surface of the ZnO NRs and SiO2/Si substrate were identified

using the Fourier transform infrared spectroscopy (FTIR, PerkinElmer Spectrum 400 spectrometer, PerkinElmer, Waltham, MA, USA). A UV-visible-near-infrared spectrophotometer from PerkinElmer was used to study the optical properties of the ZnO NRs at RT. In addition, the optical and luminescence properties of the ZnO NRs were studied through photoluminescence (PL, Horiba Fluorolog-3 for PL spectroscopy, HORIBA Jobin Yvon Inc., USA). Results and discussion SEM characterization The top-view SEM images of the ZnO NRs that were synthesized with the use of different solvents are shown in Figure 3. All of the synthesized ZnO NRs showed a hexagonal-faceted morphology. The diameter of the obtained ZnO NRs was approximately 20 to 50 nm.